Investigation of chloride stress corrosion cracking in austenitic stainless steel

Chloride stress corrosion cracking (CSCC) of AISI 304 austenitic stainless steel are the most important corrosion processes that affect the performance of this stainless steel. SCC occurs when susceptible material under the stress is exposed to a specific environment such as corrosive environment. S...

Full description

Bibliographic Details
Main Author:	Mohamad Khairuazlan, Kamaruzaman
Format:	Undergraduates Project Papers
Language:	English
Published:	2013
Subjects:	TA Engineering (General). Civil engineering (General)
Online Access:	http://umpir.ump.edu.my/id/eprint/8467/ http://umpir.ump.edu.my/id/eprint/8467/ http://umpir.ump.edu.my/id/eprint/8467/1/cd8173.pdf

id	ump-8467
recordtype	eprints
spelling	ump-84672015-11-13T02:07:10Z http://umpir.ump.edu.my/id/eprint/8467/ Investigation of chloride stress corrosion cracking in austenitic stainless steel Mohamad Khairuazlan, Kamaruzaman TA Engineering (General). Civil engineering (General) Chloride stress corrosion cracking (CSCC) of AISI 304 austenitic stainless steel are the most important corrosion processes that affect the performance of this stainless steel. SCC occurs when susceptible material under the stress is exposed to a specific environment such as corrosive environment. Since austenitic stainless steel are widely used in power boiler, nuclear power, chemical plant and marine industry, SCC can cause a major losses to these industry. The purpose of this project is to study the effect of chloride stress corrosion cracking in austenitic stainless steel based on the sensitization treatment of the specimens and different concentration mixtures of sulphuric acid and sodium chloride. Method use in this study was weight loss method. From the measurement and experiment result, it shows that mass loss for specimens with sensitization treatments is higher than mass loss for specimens without sensitization treatment. The experimental result also indicates that SCC occurs only at certain concentration mixtures of sulphuric acid and sodium chloride. This was confirmed by using scanning electron microscope and digital weighing balance. 2013-06 Undergraduates Project Papers NonPeerReviewed application/pdf en http://umpir.ump.edu.my/id/eprint/8467/1/cd8173.pdf Mohamad Khairuazlan, Kamaruzaman (2013) Investigation of chloride stress corrosion cracking in austenitic stainless steel. Faculty of Mechanical Engineering, Universiti Malaysia Pahang. http://iportal.ump.edu.my/lib/item?id=chamo:83086&theme=UMP2
repository_type	Digital Repository
institution_category	Local University
institution	Universiti Malaysia Pahang
building	UMP Institutional Repository
collection	Online Access
language	English
topic	TA Engineering (General). Civil engineering (General)
spellingShingle	TA Engineering (General). Civil engineering (General) Mohamad Khairuazlan, Kamaruzaman Investigation of chloride stress corrosion cracking in austenitic stainless steel
description	Chloride stress corrosion cracking (CSCC) of AISI 304 austenitic stainless steel are the most important corrosion processes that affect the performance of this stainless steel. SCC occurs when susceptible material under the stress is exposed to a specific environment such as corrosive environment. Since austenitic stainless steel are widely used in power boiler, nuclear power, chemical plant and marine industry, SCC can cause a major losses to these industry. The purpose of this project is to study the effect of chloride stress corrosion cracking in austenitic stainless steel based on the sensitization treatment of the specimens and different concentration mixtures of sulphuric acid and sodium chloride. Method use in this study was weight loss method. From the measurement and experiment result, it shows that mass loss for specimens with sensitization treatments is higher than mass loss for specimens without sensitization treatment. The experimental result also indicates that SCC occurs only at certain concentration mixtures of sulphuric acid and sodium chloride. This was confirmed by using scanning electron microscope and digital weighing balance.
format	Undergraduates Project Papers
author	Mohamad Khairuazlan, Kamaruzaman
author_facet	Mohamad Khairuazlan, Kamaruzaman
author_sort	Mohamad Khairuazlan, Kamaruzaman
title	Investigation of chloride stress corrosion cracking in austenitic stainless steel
title_short	Investigation of chloride stress corrosion cracking in austenitic stainless steel
title_full	Investigation of chloride stress corrosion cracking in austenitic stainless steel
title_fullStr	Investigation of chloride stress corrosion cracking in austenitic stainless steel
title_full_unstemmed	Investigation of chloride stress corrosion cracking in austenitic stainless steel
title_sort	investigation of chloride stress corrosion cracking in austenitic stainless steel
publishDate	2013
url	http://umpir.ump.edu.my/id/eprint/8467/ http://umpir.ump.edu.my/id/eprint/8467/ http://umpir.ump.edu.my/id/eprint/8467/1/cd8173.pdf
first_indexed	2023-09-18T22:06:04Z
last_indexed	2023-09-18T22:06:04Z
_version_	1777414716254060544

Investigation of chloride stress corrosion cracking in austenitic stainless steel

Similar Items