Electrochemical Behaviour of High Stress Steel (AISI 4340) in CO2 Environments with the Presence of H2 Gas
This research studied effects of CO2 and H2 gases on electrochemical behaviour of high stress steel (HSS) by using scan polarization graph to measure corrosion rate, corrosion potential and pitting potential. The tensile test samples with and without notches were tested under constant stress of 20%...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English English |
| Published: |
Trans Tech Publications, Switzerland
2014
|
| Subjects: | |
| Online Access: | http://umpir.ump.edu.my/id/eprint/6726/ http://umpir.ump.edu.my/id/eprint/6726/ http://umpir.ump.edu.my/id/eprint/6726/ http://umpir.ump.edu.my/id/eprint/6726/1/Electrochemucal_Behaviour_HSS.pdf http://umpir.ump.edu.my/id/eprint/6726/4/fkm-2014-ypanca-%20Electrochemical%20Behaviour%20of%20High.pdf |
| id |
ump-6726 |
|---|---|
| recordtype |
eprints |
| spelling |
ump-67262018-02-14T06:32:30Z http://umpir.ump.edu.my/id/eprint/6726/ Electrochemical Behaviour of High Stress Steel (AISI 4340) in CO2 Environments with the Presence of H2 Gas Asmara, Y. P. Siregar, J. P. Tezara, C. Juliawati, Alias TJ Mechanical engineering and machinery TP Chemical technology This research studied effects of CO2 and H2 gases on electrochemical behaviour of high stress steel (HSS) by using scan polarization graph to measure corrosion rate, corrosion potential and pitting potential. The tensile test samples with and without notches were tested under constant stress of 20% and immersed in 3% NaCl solutions. During experiments, CO2 gas was injected into the samples. To generate H2 gas, the samples were employed cathodically over potential at - 1700 mV (Ag/AgCl) for three days. The results indicated that both CO2 and H2 gases have increased the corrosion rate. Potentiodynamic graph showed that there were changes in pitting potential where the effect of CO2 gas would decrease the pitting potential. However,the presence of the notch did not show any significant difference in corrosion rate. Trans Tech Publications, Switzerland 2014 Article PeerReviewed application/pdf en http://umpir.ump.edu.my/id/eprint/6726/1/Electrochemucal_Behaviour_HSS.pdf application/pdf en http://umpir.ump.edu.my/id/eprint/6726/4/fkm-2014-ypanca-%20Electrochemical%20Behaviour%20of%20High.pdf Asmara, Y. P. and Siregar, J. P. and Tezara, C. and Juliawati, Alias (2014) Electrochemical Behaviour of High Stress Steel (AISI 4340) in CO2 Environments with the Presence of H2 Gas. Applied Mechanics and Materials, 695. pp. 98-101. ISSN 1662-7482 http://www.scientific.net/AMM.695.98 DOI: 10.4028/www.scientific.net/AMM.695.98 |
| repository_type |
Digital Repository |
| institution_category |
Local University |
| institution |
Universiti Malaysia Pahang |
| building |
UMP Institutional Repository |
| collection |
Online Access |
| language |
English English |
| topic |
TJ Mechanical engineering and machinery TP Chemical technology |
| spellingShingle |
TJ Mechanical engineering and machinery TP Chemical technology Asmara, Y. P. Siregar, J. P. Tezara, C. Juliawati, Alias Electrochemical Behaviour of High Stress Steel (AISI 4340) in CO2 Environments with the Presence of H2 Gas |
| description |
This research studied effects of CO2 and H2 gases on electrochemical behaviour of high stress steel (HSS) by using scan polarization graph to measure corrosion rate, corrosion potential and pitting potential. The tensile test samples with and without notches were tested under constant stress of 20% and immersed in 3% NaCl solutions. During experiments, CO2 gas was injected into the samples. To generate H2 gas, the samples were employed cathodically over potential at - 1700 mV (Ag/AgCl) for three days. The results indicated that both CO2 and H2 gases have increased the corrosion rate. Potentiodynamic graph showed that there were changes in pitting potential where the effect of CO2 gas would decrease the pitting potential. However,the presence of the notch did not show any significant difference in corrosion rate. |
| format |
Article |
| author |
Asmara, Y. P. Siregar, J. P. Tezara, C. Juliawati, Alias |
| author_facet |
Asmara, Y. P. Siregar, J. P. Tezara, C. Juliawati, Alias |
| author_sort |
Asmara, Y. P. |
| title |
Electrochemical Behaviour of High Stress Steel (AISI 4340) in CO2 Environments with the Presence of H2 Gas |
| title_short |
Electrochemical Behaviour of High Stress Steel (AISI 4340) in CO2 Environments with the Presence of H2 Gas |
| title_full |
Electrochemical Behaviour of High Stress Steel (AISI 4340) in CO2 Environments with the Presence of H2 Gas |
| title_fullStr |
Electrochemical Behaviour of High Stress Steel (AISI 4340) in CO2 Environments with the Presence of H2 Gas |
| title_full_unstemmed |
Electrochemical Behaviour of High Stress Steel (AISI 4340) in CO2 Environments with the Presence of H2 Gas |
| title_sort |
electrochemical behaviour of high stress steel (aisi 4340) in co2 environments with the presence of h2 gas |
| publisher |
Trans Tech Publications, Switzerland |
| publishDate |
2014 |
| url |
http://umpir.ump.edu.my/id/eprint/6726/ http://umpir.ump.edu.my/id/eprint/6726/ http://umpir.ump.edu.my/id/eprint/6726/ http://umpir.ump.edu.my/id/eprint/6726/1/Electrochemucal_Behaviour_HSS.pdf http://umpir.ump.edu.my/id/eprint/6726/4/fkm-2014-ypanca-%20Electrochemical%20Behaviour%20of%20High.pdf |
| first_indexed |
2023-09-18T22:02:44Z |
| last_indexed |
2023-09-18T22:02:44Z |
| _version_ |
1777414506639523840 |