Aspects of Wear Mechanisms of Carbide Tools when Machine Hastelloy C-22HS

In this study the performances of some commercially available carbide inserts when machining Hastelloy C-22HS was investigated under scanning electron microscopy (SEM) for wear mechanisms and other microstructure defects. Carbide inserts coated with TiCN/TiN and TiALN/ TiN experienced severe intergr...

Full description

Bibliographic Details
Main Authors:	K., Kadirgama, M. M., Noor, B., Mohammad, H. H., Habeeb
Format:	Article
Language:	English
Published:	2010
Subjects:	TJ Mechanical engineering and machinery
Online Access:	http://umpir.ump.edu.my/id/eprint/2248/ http://umpir.ump.edu.my/id/eprint/2248/ http://umpir.ump.edu.my/id/eprint/2248/1/Aspects_of_Wear_Mechanisms_of_Carbide_Tools_when_Machine.pdf

id	ump-2248
recordtype	eprints
spelling	ump-22482018-01-31T00:55:37Z http://umpir.ump.edu.my/id/eprint/2248/ Aspects of Wear Mechanisms of Carbide Tools when Machine Hastelloy C-22HS K., Kadirgama M. M., Noor B., Mohammad H. H., Habeeb TJ Mechanical engineering and machinery In this study the performances of some commercially available carbide inserts when machining Hastelloy C-22HS was investigated under scanning electron microscopy (SEM) for wear mechanisms and other microstructure defects. Carbide inserts coated with TiCN/TiN and TiALN/ TiN experienced severe intergranular fractures and cracks. High temperature causes the layer of the coating to wear off and subsequently the inserts damaged at fast rates. Both types of inserts suffered from high crater wear and thermal cracking. Most of the wear occurred at the nose and flank of the inserts. Generally, it was observed that carbide coated with TiALN/ TiN cutting tool performed better than carbide coated TiCN/TiN cutting tool when milling Hastelloy C-22HS 2010 Article PeerReviewed application/pdf en http://umpir.ump.edu.my/id/eprint/2248/1/Aspects_of_Wear_Mechanisms_of_Carbide_Tools_when_Machine.pdf K., Kadirgama and M. M., Noor and B., Mohammad and H. H., Habeeb (2010) Aspects of Wear Mechanisms of Carbide Tools when Machine Hastelloy C-22HS. Advanced Materials Research, 83-86 . pp. 295-302. ISSN 1022-6680 http://www.scientific.net/AMR.83-86.295
repository_type	Digital Repository
institution_category	Local University
institution	Universiti Malaysia Pahang
building	UMP Institutional Repository
collection	Online Access
language	English
topic	TJ Mechanical engineering and machinery
spellingShingle	TJ Mechanical engineering and machinery K., Kadirgama M. M., Noor B., Mohammad H. H., Habeeb Aspects of Wear Mechanisms of Carbide Tools when Machine Hastelloy C-22HS
description	In this study the performances of some commercially available carbide inserts when machining Hastelloy C-22HS was investigated under scanning electron microscopy (SEM) for wear mechanisms and other microstructure defects. Carbide inserts coated with TiCN/TiN and TiALN/ TiN experienced severe intergranular fractures and cracks. High temperature causes the layer of the coating to wear off and subsequently the inserts damaged at fast rates. Both types of inserts suffered from high crater wear and thermal cracking. Most of the wear occurred at the nose and flank of the inserts. Generally, it was observed that carbide coated with TiALN/ TiN cutting tool performed better than carbide coated TiCN/TiN cutting tool when milling Hastelloy C-22HS
format	Article
author	K., Kadirgama M. M., Noor B., Mohammad H. H., Habeeb
author_facet	K., Kadirgama M. M., Noor B., Mohammad H. H., Habeeb
author_sort	K., Kadirgama
title	Aspects of Wear Mechanisms of Carbide Tools when Machine Hastelloy C-22HS
title_short	Aspects of Wear Mechanisms of Carbide Tools when Machine Hastelloy C-22HS
title_full	Aspects of Wear Mechanisms of Carbide Tools when Machine Hastelloy C-22HS
title_fullStr	Aspects of Wear Mechanisms of Carbide Tools when Machine Hastelloy C-22HS
title_full_unstemmed	Aspects of Wear Mechanisms of Carbide Tools when Machine Hastelloy C-22HS
title_sort	aspects of wear mechanisms of carbide tools when machine hastelloy c-22hs
publishDate	2010
url	http://umpir.ump.edu.my/id/eprint/2248/ http://umpir.ump.edu.my/id/eprint/2248/ http://umpir.ump.edu.my/id/eprint/2248/1/Aspects_of_Wear_Mechanisms_of_Carbide_Tools_when_Machine.pdf
first_indexed	2023-09-18T21:55:53Z
last_indexed	2023-09-18T21:55:53Z
_version_	1777414075089682432

Aspects of Wear Mechanisms of Carbide Tools when Machine Hastelloy C-22HS

Similar Items