Effect of ZnO addition on structural properties of ZnO-PANi/carbon black thin films
The aim of this project was to investigate the effect of ZnO addition on the structural properties of ZnO-PANi/carbon black thin films. The sol gel method was employed for the preparation of ZnO sol. The sol was dried for 24 h at 100°C and then annealed at 600°C for 5 h. XRD characterization of the...
| Main Authors: | , , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Universiti Kebangsaan Malaysia
2012
|
| Online Access: | http://journalarticle.ukm.my/5421/ http://journalarticle.ukm.my/5421/ http://journalarticle.ukm.my/5421/1/09%2520siti%2520fariza.pdf |
| Summary: | The aim of this project was to investigate the effect of ZnO addition on the structural properties of ZnO-PANi/carbon black thin films. The sol gel method was employed for the preparation of ZnO sol. The sol was dried for 24 h at 100°C and then annealed at 600°C for 5 h. XRD characterization of the ZnO powder showed the formation of wurtzite type ZnO crystals. The ZnO powder were mixed into PANi/carbon black solution which was dissolved into M-Pyrol, N-Methyl-2-Pyrrolidinone (NMP) to produce a composite solution of ZnO-PANi/carbon black. The weight ratio of ZnO were 4 wt%, 6 wt% and 8 wt%. The composite solutions were deposited onto glass substrates using a spin-coating technique to fabricate ZnO-PANi/carbon black thin films. AFM characterization showed the decreasing of average roughness from 7.98 nm to 2.23 nm with the increment of ZnO addition in PANi/carbon black films. The thickness of the films also decreased from 59.5 nm to 28.3 nm. FESEM image revealed that ZnO-PANi/carbon black thin films have changed into agglomerated surface morphology resulting in the increment of porosity of the films. |
|---|