Electrochemical behaviour of Ni and Ni-PVC electrodes for the electroxidation of ethanol (Tingkah Laku Elektrokimia Pengoksidaan Etanol Menggunakan Elektrod Ni dan Ni-PVC)
In this study, two nickel based electrodes were prepared; nickel foil and nickel-polyvinylchloride (Ni-PVC), in order to study their electrochemical behavior using cyclic voltammetry, CV and chronocoulometry, CC. Ni electrode was prepared from Ni metal foil while Ni-PVC electrode was prepared by mix...
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Universiti Kebangsaan Malaysia
2011
|
| Online Access: | http://journalarticle.ukm.my/3143/ http://journalarticle.ukm.my/3143/ http://journalarticle.ukm.my/3143/1/12_Mohd_Syafiq.pdf |
| Summary: | In this study, two nickel based electrodes were prepared; nickel foil and nickel-polyvinylchloride (Ni-PVC), in order to study their electrochemical behavior using cyclic voltammetry, CV and chronocoulometry, CC. Ni electrode was prepared from Ni metal foil while Ni-PVC electrode was prepared by mixing a weighed portion of Ni powder and PVC in THF solvent, swirled until the suspension was homogeneous and drying the suspension in an oven at 50oC for 3 h. The dry sample was then placed in a 1 cm diameter stainless steel mould and pressed at 10 ton/cm2. From CV data, Ni-PVC electrode showed a better electrochemical behavior compared to Ni metal foil electrode. The use of Ni-PVC electrode at higher concentration of supporting electrolyte (1.0 M KOH) was better than at lower concentration of the same supporting electrolyte in electroxidation of ethanol. In addition to acetic acid, the oxidation of ethanol also produced ethyl acetate and acetaldehyde. |
|---|