The production of biodiesel from palm oil catalysed by calcium oxide (cao) and potassium iodide (ki) supported on alumina beads / Nur Amirah Azmi
Biodiesel is one of the green fuels and alternative to petroleum based fuel. It is environmental friendly and emits less pollutants into the air. In this research, the biodiesel was produced from the palm oil by the transesterification reaction catalyzed by calcium oxide (CaO) and potassium iodid...
| Main Author: | |
|---|---|
| Format: | Student Project |
| Language: | English |
| Published: |
Faculty Of Applied Sciences
2019
|
| Subjects: | |
| Online Access: | http://ir.uitm.edu.my/id/eprint/25231/ http://ir.uitm.edu.my/id/eprint/25231/1/PPb_NUR%20AMIRAH%20AZMI%20AS%20C%2019_5.PDF |
| Summary: | Biodiesel is one of the green fuels and alternative to petroleum based fuel. It is
environmental friendly and emits less pollutants into the air. In this research, the
biodiesel was produced from the palm oil by the transesterification reaction
catalyzed by calcium oxide (CaO) and potassium iodide (KI) supported on alumina
beads (CaO/KI/AI2O3). The main objectives of this study were to determine the
optimum loading of catalyst and the effect of nickel as dopant for CaO/Kl/AI2O3.
Two types of catalyst were prepared which are the nickel doped calcium oxide potassium
iodide-alumina (Ni-doped CaO/KI/AI2O3) and undoped calcium oxidepotassium
iodide-alumina (CaO/KI/AI2O3). The transesterification reactions were
carried out at 65°C for 5 hours using a mixture of palm oil and methanol with mass
ratio 1:9 with different catalyst loadings between I% to 6%. The biodiesel yield for
all samples were determined by using the gas chromatography-mass spectrometry
(GCMS). For the Ni-doped CaO/KI/AI2O3) the optimum catalyst loading was 2%
which produced 5.55% biodiesel yield while for the undoped CaO/KI/AI2O3 the
optimum catalyst loading was 6% with 3.34% biodiesel yield. The biodiesel yield
for the sample loaded with undoped catalyst generally increased with the amount
of catalyst added. While for the Ni-doped catalyst the biodiesel yield increased
until 2% catalyst loading but then decreased when added with 3% to 6% of catalyst
this was due to the leaching of catalyst had disrupt the catalytic activity. Overall
the biodiesel was successfully produced from palm oil by using both doped and
undoped (CaO/KI/AI2O3) catalyst and it can be concluded that undoped catalyst had
a better catalytic activity as it produced higher biodiesel compared to Ni-doped
catalyst. |
|---|