The evaluation and comparison of properties of particleboard made from kenaf / Nor Shuhada Abdullah
This project was carried out to evaluate and compare the properties of particleboard made from kenaf Boards are prepared for mechanical and physical tests. Results were summarized and analyses using ANOVA. The target board density was 600kglm3 and resin content of Phenol Formaldehyde that used is...
| Main Author: | |
|---|---|
| Format: | Student Project |
| Language: | English |
| Published: |
Faculty Of Applied Sciences
2014
|
| Subjects: | |
| Online Access: | http://ir.uitm.edu.my/id/eprint/22830/ http://ir.uitm.edu.my/id/eprint/22830/1/PPb_NOR%20SHUHADA%20ABDULLAH%20AS%20C%2014_5.PDF |
| Summary: | This project was carried out to evaluate and compare the properties of particleboard
made from kenaf Boards are prepared for mechanical and physical tests. Results
were summarized and analyses using ANOVA. The target board density was
600kglm3 and resin content of Phenol Formaldehyde that used is 7% and 11%. The
experimental panels were evaluated by determine the modulus of ruptured (MOR) ,
modulus of elasticity (MOE), internal bonding strength (IB), water absorption (WA)
and thickness swelling (TS) based on British Standard (BS). The test result for
mechanical properties showed that the MOE, MOR and m values did not meet
standard requirements but it is still can improve it. As a conclusion, the kenaf core
can be used as a raw material for particleboard manufacturing. |
|---|