Effect of Alᶟ⁺ substitutions at Cu-site and AI₂O₃ addition on ultrasonic velocities and elasticanomalies of EuBa₂Cu₃O₇-ᵟ uperconductor / Mohd Muzammir Firdaus Abu Bakar
The ultrasonic longitudinal and shear velocities were measured in EuBa₂Cu₃O₇₋₈ (δ = 0.1 and 0.7), EuBa₂Cu₃₋ₓA1ₓO₇₋₈ (х = 0.06 and 0.1) and EuBa₂Cu₃O₇₋₈ + yA1₂O₃ (y = 0.2 and 0.1 wt%) superconductors in temperature ranges of 80-280K and 80-220K, respectively. For EuBa₂Cu₃O₇₋₈ (δ = 0.1 and 0.7), sampl...
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | English |
| Published: |
2013
|
| Online Access: | http://ir.uitm.edu.my/id/eprint/18465/ http://ir.uitm.edu.my/id/eprint/18465/2/TM_MOHD%20MUZAMMIR%20FIRDAUS%20ABU%20BAKAR%20AS%2013_5.pdf |
| id |
uitm-18465 |
|---|---|
| recordtype |
eprints |
| spelling |
uitm-184652019-02-04T06:05:25Z http://ir.uitm.edu.my/id/eprint/18465/ Effect of Alᶟ⁺ substitutions at Cu-site and AI₂O₃ addition on ultrasonic velocities and elasticanomalies of EuBa₂Cu₃O₇-ᵟ uperconductor / Mohd Muzammir Firdaus Abu Bakar Abu Bakar, Mohd Muzammir Firdaus The ultrasonic longitudinal and shear velocities were measured in EuBa₂Cu₃O₇₋₈ (δ = 0.1 and 0.7), EuBa₂Cu₃₋ₓA1ₓO₇₋₈ (х = 0.06 and 0.1) and EuBa₂Cu₃O₇₋₈ + yA1₂O₃ (y = 0.2 and 0.1 wt%) superconductors in temperature ranges of 80-280K and 80-220K, respectively. For EuBa₂Cu₃O₇₋₈ (δ = 0.1 and 0.7), samples, the absolute velocity (at 80K) showed to decrease when the oxygen content was reduced from O6.9 to O6.3 . However, for EuBa₂Cu₃₋ₓA1ₓO₇₋₈ (х = 0.06 and 0.1)) samples, although both samples have same oxygen content (O6.8), the absolute velocity also showed to decrease when the amount of A1ᶟ⁺ increased… 2013 Thesis NonPeerReviewed text en http://ir.uitm.edu.my/id/eprint/18465/2/TM_MOHD%20MUZAMMIR%20FIRDAUS%20ABU%20BAKAR%20AS%2013_5.pdf Abu Bakar, Mohd Muzammir Firdaus (2013) Effect of Alᶟ⁺ substitutions at Cu-site and AI₂O₃ addition on ultrasonic velocities and elasticanomalies of EuBa₂Cu₃O₇-ᵟ uperconductor / Mohd Muzammir Firdaus Abu Bakar. Masters thesis, Universiti Teknologi MARA. |
| repository_type |
Digital Repository |
| institution_category |
Local University |
| institution |
Universiti Teknologi MARA |
| building |
UiTM Institutional Repository |
| collection |
Online Access |
| language |
English |
| description |
The ultrasonic longitudinal and shear velocities were measured in EuBa₂Cu₃O₇₋₈ (δ = 0.1 and 0.7), EuBa₂Cu₃₋ₓA1ₓO₇₋₈ (х = 0.06 and 0.1) and EuBa₂Cu₃O₇₋₈ + yA1₂O₃ (y = 0.2 and 0.1 wt%) superconductors in temperature ranges of 80-280K and 80-220K, respectively. For EuBa₂Cu₃O₇₋₈ (δ = 0.1 and 0.7), samples, the absolute velocity (at 80K) showed to decrease when the oxygen content was reduced from O6.9 to O6.3 . However, for EuBa₂Cu₃₋ₓA1ₓO₇₋₈ (х = 0.06 and 0.1)) samples, although both samples have same oxygen content (O6.8), the absolute velocity also showed to decrease when the amount of A1ᶟ⁺ increased… |
| format |
Thesis |
| author |
Abu Bakar, Mohd Muzammir Firdaus |
| spellingShingle |
Abu Bakar, Mohd Muzammir Firdaus Effect of Alᶟ⁺ substitutions at Cu-site and AI₂O₃ addition on ultrasonic velocities and elasticanomalies of EuBa₂Cu₃O₇-ᵟ uperconductor / Mohd Muzammir Firdaus Abu Bakar |
| author_facet |
Abu Bakar, Mohd Muzammir Firdaus |
| author_sort |
Abu Bakar, Mohd Muzammir Firdaus |
| title |
Effect of Alᶟ⁺ substitutions at Cu-site and AI₂O₃ addition on ultrasonic velocities and elasticanomalies of EuBa₂Cu₃O₇-ᵟ uperconductor / Mohd Muzammir Firdaus Abu Bakar |
| title_short |
Effect of Alᶟ⁺ substitutions at Cu-site and AI₂O₃ addition on ultrasonic velocities and elasticanomalies of EuBa₂Cu₃O₇-ᵟ uperconductor / Mohd Muzammir Firdaus Abu Bakar |
| title_full |
Effect of Alᶟ⁺ substitutions at Cu-site and AI₂O₃ addition on ultrasonic velocities and elasticanomalies of EuBa₂Cu₃O₇-ᵟ uperconductor / Mohd Muzammir Firdaus Abu Bakar |
| title_fullStr |
Effect of Alᶟ⁺ substitutions at Cu-site and AI₂O₃ addition on ultrasonic velocities and elasticanomalies of EuBa₂Cu₃O₇-ᵟ uperconductor / Mohd Muzammir Firdaus Abu Bakar |
| title_full_unstemmed |
Effect of Alᶟ⁺ substitutions at Cu-site and AI₂O₃ addition on ultrasonic velocities and elasticanomalies of EuBa₂Cu₃O₇-ᵟ uperconductor / Mohd Muzammir Firdaus Abu Bakar |
| title_sort |
effect of alᶟ⁺ substitutions at cu-site and ai₂o₃ addition on ultrasonic velocities and elasticanomalies of euba₂cu₃o₇-ᵟ uperconductor / mohd muzammir firdaus abu bakar |
| publishDate |
2013 |
| url |
http://ir.uitm.edu.my/id/eprint/18465/ http://ir.uitm.edu.my/id/eprint/18465/2/TM_MOHD%20MUZAMMIR%20FIRDAUS%20ABU%20BAKAR%20AS%2013_5.pdf |
| first_indexed |
2023-09-18T23:00:35Z |
| last_indexed |
2023-09-18T23:00:35Z |
| _version_ |
1777418146457583616 |