Zinc oxide nanorods as electron transport layer in MEH-PPV/ZnO organic light emitting diodes / Shafinaz Sobihana Shariffudin

This thesis discusses on the development of zinc oxide (ZnO) nanorods for the application as electron transport layer in MEH-PPV/ZnO Organic Light Emitting Diode (OLED). In general, the mobility of holes is higher than electrons in most semiconducting organic material. Therefore, it is essential to...

Full description

Bibliographic Details
Main Author:	Shariffudin, Shafinaz Sobihana
Format:	Thesis
Language:	English
Published:	2016
Online Access:	http://ir.uitm.edu.my/id/eprint/17722/ http://ir.uitm.edu.my/id/eprint/17722/1/TP_SHAFINAZ%20SOBIHANA%20SHARIFFUDDIN%20EE%2016_5.pdf

id	uitm-17722
recordtype	eprints
spelling	uitm-177222018-09-24T06:37:49Z http://ir.uitm.edu.my/id/eprint/17722/ Zinc oxide nanorods as electron transport layer in MEH-PPV/ZnO organic light emitting diodes / Shafinaz Sobihana Shariffudin Shariffudin, Shafinaz Sobihana This thesis discusses on the development of zinc oxide (ZnO) nanorods for the application as electron transport layer in MEH-PPV/ZnO Organic Light Emitting Diode (OLED). In general, the mobility of holes is higher than electrons in most semiconducting organic material. Therefore, it is essential to develop an efficient electron transport layer in order to balance out the number of carriers, hence increases the efficiency of the device. Furthermore, combining inorganic material with organic material in a device can take advantages of both materials. The thesis work involved three main parts for the fabrication of MEH-PPV/ZnO OLEDs. The first part was the deposition of novel layer-by-layer ZnO seeded catalyst. High (0 0 2) oaxis ZnO seed catalyst was prepared using simple and low cost method of sol-gel spin coating technique. Layer-by-layer method was applied in the deposition of the ZnO seed catalyst layer, which is defined by annealing of every layer of the thin film. The second part involved the growth of ZnO nanorods using thermal chemical vapour deposition (TCVD) method by employing vapour-solid (VS) mechanism, without using pump vacuum to control the pressure in the tube. Using single furnace TCVD, substrate positions with a distance of 3 cm from the zinc powder, at an oxygen flow rate of 5 seem and temperature of 825°C were found to be the optimum conditions for the growth of the ZnO nanorods in this study. The characterization revealed that the nanorods had low resistivity of 5 x 10⁻² Ω-cm at highest (0 0 2) crystalline structure. This strongly indicates that the ZnO nanorods had good electrical behaviour which can transport electrons more efficiently in the device. Third part involved the study of MEH-PPV thin films dissolved in non-aromatic solvent such as 1,2 dichlorobenzene and toluene to produce p-type conducting emissive layer. With an optimum solution concentration of 5 mg/ml, highest photoluminescence (PL) spectrum was produced with an emission centred at 590 nm. From the optimized thin films, OLEDs were fabricated. As a conclusion, by combining the ZnO nanorods with MEH-PPV in the OLEDs had improved the electrical characteristics of the device compared to single layer MEH-PPV based device. The fabricated device worked as a diode; which showed a rectifying current. The lowest turn on voltage was found to be at 0.4V using the ZnO nanorods grown at temperature of 825°C. At this deposition temperature, the Schottky barrier height was 0.59 eV, with an ideality factor of 12.91. The OLEDs were also tested using electroluminescence (EL) spectroscopy to prove the devices' functionality. The EL emission spectra were found to match with the PL emission for both ZnO and MEH-PPV thin films. 2016 Thesis NonPeerReviewed text en http://ir.uitm.edu.my/id/eprint/17722/1/TP_SHAFINAZ%20SOBIHANA%20SHARIFFUDDIN%20EE%2016_5.pdf Shariffudin, Shafinaz Sobihana (2016) Zinc oxide nanorods as electron transport layer in MEH-PPV/ZnO organic light emitting diodes / Shafinaz Sobihana Shariffudin. PhD thesis, Universiti Teknologi MARA.
repository_type	Digital Repository
institution_category	Local University
institution	Universiti Teknologi MARA
building	UiTM Institutional Repository
collection	Online Access
language	English
description	This thesis discusses on the development of zinc oxide (ZnO) nanorods for the application as electron transport layer in MEH-PPV/ZnO Organic Light Emitting Diode (OLED). In general, the mobility of holes is higher than electrons in most semiconducting organic material. Therefore, it is essential to develop an efficient electron transport layer in order to balance out the number of carriers, hence increases the efficiency of the device. Furthermore, combining inorganic material with organic material in a device can take advantages of both materials. The thesis work involved three main parts for the fabrication of MEH-PPV/ZnO OLEDs. The first part was the deposition of novel layer-by-layer ZnO seeded catalyst. High (0 0 2) oaxis ZnO seed catalyst was prepared using simple and low cost method of sol-gel spin coating technique. Layer-by-layer method was applied in the deposition of the ZnO seed catalyst layer, which is defined by annealing of every layer of the thin film. The second part involved the growth of ZnO nanorods using thermal chemical vapour deposition (TCVD) method by employing vapour-solid (VS) mechanism, without using pump vacuum to control the pressure in the tube. Using single furnace TCVD, substrate positions with a distance of 3 cm from the zinc powder, at an oxygen flow rate of 5 seem and temperature of 825°C were found to be the optimum conditions for the growth of the ZnO nanorods in this study. The characterization revealed that the nanorods had low resistivity of 5 x 10⁻² Ω-cm at highest (0 0 2) crystalline structure. This strongly indicates that the ZnO nanorods had good electrical behaviour which can transport electrons more efficiently in the device. Third part involved the study of MEH-PPV thin films dissolved in non-aromatic solvent such as 1,2 dichlorobenzene and toluene to produce p-type conducting emissive layer. With an optimum solution concentration of 5 mg/ml, highest photoluminescence (PL) spectrum was produced with an emission centred at 590 nm. From the optimized thin films, OLEDs were fabricated. As a conclusion, by combining the ZnO nanorods with MEH-PPV in the OLEDs had improved the electrical characteristics of the device compared to single layer MEH-PPV based device. The fabricated device worked as a diode; which showed a rectifying current. The lowest turn on voltage was found to be at 0.4V using the ZnO nanorods grown at temperature of 825°C. At this deposition temperature, the Schottky barrier height was 0.59 eV, with an ideality factor of 12.91. The OLEDs were also tested using electroluminescence (EL) spectroscopy to prove the devices' functionality. The EL emission spectra were found to match with the PL emission for both ZnO and MEH-PPV thin films.
format	Thesis
author	Shariffudin, Shafinaz Sobihana
spellingShingle	Shariffudin, Shafinaz Sobihana Zinc oxide nanorods as electron transport layer in MEH-PPV/ZnO organic light emitting diodes / Shafinaz Sobihana Shariffudin
author_facet	Shariffudin, Shafinaz Sobihana
author_sort	Shariffudin, Shafinaz Sobihana
title	Zinc oxide nanorods as electron transport layer in MEH-PPV/ZnO organic light emitting diodes / Shafinaz Sobihana Shariffudin
title_short	Zinc oxide nanorods as electron transport layer in MEH-PPV/ZnO organic light emitting diodes / Shafinaz Sobihana Shariffudin
title_full	Zinc oxide nanorods as electron transport layer in MEH-PPV/ZnO organic light emitting diodes / Shafinaz Sobihana Shariffudin
title_fullStr	Zinc oxide nanorods as electron transport layer in MEH-PPV/ZnO organic light emitting diodes / Shafinaz Sobihana Shariffudin
title_full_unstemmed	Zinc oxide nanorods as electron transport layer in MEH-PPV/ZnO organic light emitting diodes / Shafinaz Sobihana Shariffudin
title_sort	zinc oxide nanorods as electron transport layer in meh-ppv/zno organic light emitting diodes / shafinaz sobihana shariffudin
publishDate	2016
url	http://ir.uitm.edu.my/id/eprint/17722/ http://ir.uitm.edu.my/id/eprint/17722/1/TP_SHAFINAZ%20SOBIHANA%20SHARIFFUDDIN%20EE%2016_5.pdf
first_indexed	2023-09-18T22:58:55Z
last_indexed	2023-09-18T22:58:55Z
_version_	1777418041677578240

Zinc oxide nanorods as electron transport layer in MEH-PPV/ZnO organic light emitting diodes / Shafinaz Sobihana Shariffudin

Similar Items