Bi-based mono-core superconductor tapes : fabrication process and the effect of the thermomechanical treatment on the transport properties / K.T. Lau and R-Abd Shukor

Fabrication of the Bi-based tapes started with the preparation of its precursor powder with composition of Bi1.8 Pb 0.4 Sr2 Ca2.2 Cu3 O10+y. The post-annealed powder with a majority of 2212 phase was then ground before it was packed into a silver tube. Then the composite was sway-rolled and drawn in...

Full description

Bibliographic Details
Main Authors:	Lau, K.T., R-, Abd Shukor
Format:	Article
Language:	English
Published:	Faculty of Applied Sciences 2005
Subjects:	Electricity and magnetism
Online Access:	http://ir.uitm.edu.my/id/eprint/11791/ http://ir.uitm.edu.my/id/eprint/11791/1/AJ_K.T.%20LAU%20SL%2005.pdf

id	uitm-11791
recordtype	eprints
spelling	uitm-117912016-09-06T04:59:40Z http://ir.uitm.edu.my/id/eprint/11791/ Bi-based mono-core superconductor tapes : fabrication process and the effect of the thermomechanical treatment on the transport properties / K.T. Lau and R-Abd Shukor Lau, K.T. R-, Abd Shukor Electricity and magnetism Fabrication of the Bi-based tapes started with the preparation of its precursor powder with composition of Bi1.8 Pb 0.4 Sr2 Ca2.2 Cu3 O10+y. The post-annealed powder with a majority of 2212 phase was then ground before it was packed into a silver tube. Then the composite was sway-rolled and drawn into wire with diameter of 1.08 mm. To make it into tape form, the wire was cut into shorter length before went through rolling process using a roller machine. The tapes were divided into sample groups and underwent different thermo-mechanical treatments. All the final processed Bi-based tapes had mixed superconductor phases of 2223 and 2212. Most part of HTSC grains in the tapes melted during the sintering. Transport voltage-current characteristics of the tapes was found to obey the power law relationship. The thermo-mechanical treatment was found necessary to improve the structural quality of the tapes. Faculty of Applied Sciences 2005 Article PeerReviewed text en http://ir.uitm.edu.my/id/eprint/11791/1/AJ_K.T.%20LAU%20SL%2005.pdf Lau, K.T. and R-, Abd Shukor (2005) Bi-based mono-core superconductor tapes : fabrication process and the effect of the thermomechanical treatment on the transport properties / K.T. Lau and R-Abd Shukor. Science Letters, 2 (1). pp. 41-48. ISSN 1675-7785
repository_type	Digital Repository
institution_category	Local University
institution	Universiti Teknologi MARA
building	UiTM Institutional Repository
collection	Online Access
language	English
topic	Electricity and magnetism
spellingShingle	Electricity and magnetism Lau, K.T. R-, Abd Shukor Bi-based mono-core superconductor tapes : fabrication process and the effect of the thermomechanical treatment on the transport properties / K.T. Lau and R-Abd Shukor
description	Fabrication of the Bi-based tapes started with the preparation of its precursor powder with composition of Bi1.8 Pb 0.4 Sr2 Ca2.2 Cu3 O10+y. The post-annealed powder with a majority of 2212 phase was then ground before it was packed into a silver tube. Then the composite was sway-rolled and drawn into wire with diameter of 1.08 mm. To make it into tape form, the wire was cut into shorter length before went through rolling process using a roller machine. The tapes were divided into sample groups and underwent different thermo-mechanical treatments. All the final processed Bi-based tapes had mixed superconductor phases of 2223 and 2212. Most part of HTSC grains in the tapes melted during the sintering. Transport voltage-current characteristics of the tapes was found to obey the power law relationship. The thermo-mechanical treatment was found necessary to improve the structural quality of the tapes.
format	Article
author	Lau, K.T. R-, Abd Shukor
author_facet	Lau, K.T. R-, Abd Shukor
author_sort	Lau, K.T.
title	Bi-based mono-core superconductor tapes : fabrication process and the effect of the thermomechanical treatment on the transport properties / K.T. Lau and R-Abd Shukor
title_short	Bi-based mono-core superconductor tapes : fabrication process and the effect of the thermomechanical treatment on the transport properties / K.T. Lau and R-Abd Shukor
title_full	Bi-based mono-core superconductor tapes : fabrication process and the effect of the thermomechanical treatment on the transport properties / K.T. Lau and R-Abd Shukor
title_fullStr	Bi-based mono-core superconductor tapes : fabrication process and the effect of the thermomechanical treatment on the transport properties / K.T. Lau and R-Abd Shukor
title_full_unstemmed	Bi-based mono-core superconductor tapes : fabrication process and the effect of the thermomechanical treatment on the transport properties / K.T. Lau and R-Abd Shukor
title_sort	bi-based mono-core superconductor tapes : fabrication process and the effect of the thermomechanical treatment on the transport properties / k.t. lau and r-abd shukor
publisher	Faculty of Applied Sciences
publishDate	2005
url	http://ir.uitm.edu.my/id/eprint/11791/ http://ir.uitm.edu.my/id/eprint/11791/1/AJ_K.T.%20LAU%20SL%2005.pdf
first_indexed	2023-09-18T22:48:32Z
last_indexed	2023-09-18T22:48:32Z
_version_	1777417388437798912

Bi-based mono-core superconductor tapes : fabrication process and the effect of the thermomechanical treatment on the transport properties / K.T. Lau and R-Abd Shukor

Similar Items