Effect of chilled air on tool wear and workpiece quality during milling of carbon fibre-reinforced plastic
Carbon fibre reinforced plastic (CFRP) is a composite which has the best strength to weight ratio among the construction materials. It becomes valuable as the demand for this composite has increased dramatically especially in automobile and aerospace industry. The need in these industries such as...
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Elsevier BV
2013
|
| Subjects: | |
| Online Access: | http://irep.iium.edu.my/48578/ http://irep.iium.edu.my/48578/ http://irep.iium.edu.my/48578/ http://irep.iium.edu.my/48578/1/wear_cfrp.pdf |
| Summary: | Carbon fibre reinforced plastic (CFRP) is a composite which has the best strength to weight ratio among
the construction materials. It becomes valuable as the demand for this composite has increased
dramatically especially in automobile and aerospace industry. The need in these industries such as light
weight, but retain high strength, make CFRP better choice than steel. CFRP is also known as an
expensive material, since an expensive chemical treatment is required in the fabrication process.
Therefore, the manufacturing cost of CFRPs’ parts need to be minimized, the factors that influenced the
end product’s surface quality such as cost of severe tool wear, which shortens the tool life, fibre pull-out
and delamination of CFRP need to be eliminated. Many studies on tool geometries, cutting tool
materials, and cutting parameters have been done to overcome these problems. In this study, chilled air
of −10 °C was applied to the cutting tool using a vortex tube, which is new in the machining of fibres,
to minimize the heat generated during machining. Cutting speed of 160–200 m/min and a feed rate of
0.025–0.05 mm/rev on solid uncoated carbide during the milling process were discussed. At room
temperature conditions, it is observed that the wear area is found polished and shining. Under room
temperature cutting condition, the wear region is high at higher cutting speeds and feed rates, but in
chilled air machining, these types of wear of the carbide tool are found less at higher cutting speeds and
feed rates. The improvement in tool life while applying chilled air during machining of CFRP is 1.6% and
12.1% at lowest feed rate and cutting speed; while 31.8% and 45.6% longer tool life of carbide cutting
tool is observed at highest feed rate and cutting speed under chilled air machining compared to room
temperature machining. The delamination factor of CFRP is also found to improve at higher cutting
speeds during chilled-air machining.
|
|---|